Oilart – Oil resistant rubber sheets

Oil resistant rubber sheets are made of nitrile-butadiene rubber, resistant to fuel B or blend of NBR with SBR, resistant to oil and mineral, animal and vegetal fats.

Oil resistant rubber sheets based on NBR

Excelent quality, suitable for use of  fuels and petrols.

Oilart 3.1
Colour black
Hardness°Shore A 50±5
Tensile strength(kgf/cm2)min. 75
Elongation at break %,min. 450
Compression set (24h x70°C),% max. 25
Change of volume (DV) after immersion,.%max
Fluid B(70toluene/30isooctane); test condition ,22 h x40°C
DV,% 0…+35
Working temperature,°C -25°C…+110°C
Oilart 3.2
Colour black
Hardness°Shore A 60±5
Tensile strength(kgf/cm2)min. 78
Elongation at break %,min. 400
Compression set (24h x70°C),% max. 20
Change of volume (DV) after immersion,.%max
Fluid, B(70toluene/30isooctane) ; test condition ,22 h x40°C
DV,% 0……+30
Working temperature,°C -25°C….+110°C
Oilart 3.3
Colour black
Hardness°Shore A 70±5
Tensile strength(kgf/cm2)min. 125
Elongation at break %,min. 250
Compression set (24h x70°C),% max. 20
Change of volume (DV) after immersion,.%max
Fluide B(30toluene/70isooctane); test condi]ion,22 h x 40°C
DV,% 0…+30
Working temperature,°C -25°C…+110°C
Oilart 3.4
Colour black
Hardness°Shore A 80±5
Tensile strength(kgf/cm2)min. 125
Elongation at break %,min. 150
Compression set (24h x70°C),% max. 20
Change of volume (DV) after immersion,.%max
Fluide B(30toluene/70isooctane): test condi]ion,22 h x 40°C
DV,% 0…+30
Working temperature,°C -25°C…+110°C
Oil resistant rubber sheets based on blend of SBR and  NBR

Manufactured of  styrene-butadiene and nytrile  rubber blends, indicated to used of mineral and animal oils and fats.

Oilart 3.5 – 3.6
Colour black
Hardness°Shore A 3.5 -70±5; 3.6 -80±5
Tensile strength(kgf/cm2)min. 50
Elongation at break %,min. 200
Compression set (24h x70°C),% max. 40
Density ,g/cm3 1,35
Change of volume (DV) after immersion,.%max
ASTM oil nr. 3
Test condi]ion, 70 h x 100°C
DV,% 0…+30
Working temperature,°C -30°C…+110°C
Oilart 3.7
Colour black
Hardness°Shore A 50±5
Tensile strength(kgf/cm2)min. 40
Elongation at break %,min. 200
Compression set (24h x70°C),% max. 40
Density ,g/cm3 1,3
Change of volume (DV) after immersion,.%max
ASTM oil nr.3
Test condition, 70 h x 100°C
DV,% 0…+30
Working temperature,°C -30°C…+110°C